Sandvik
2RE10
Read this notice
Seamless tube and pipe
Build Datasheet
At 20
°
C (68
°
F)
Metric units
Proof strength
R
p0.2
a)
MPa
min.
R
p
1.0
a)
MPa
min.
Tensile strength
R
m
MPa
min.
Elong.
A
b)
%
min.
Hardness
Vickers
approx.
210
240
500-670
35
c)
155
Imperial units
Proof strength
R
p0.2
a)
ksi
min.
R
p1.0
a)
ksi
min.
Tensile strength
R
m
ksi
min.
Elong.
A
b)
%
min.
Hardness
Vickers
approx.
30
35
73-98
35
c)
155
1 MPa = 1 N/mm
2
a) R
p0.2
and R
p1.0
correspond to 0.2% offset yield strength respectively.
b) Based on L
0
= 5.65
Ö
S
0
, where L
0
is the original gauge length and S
0
the original cross-section area.
c) EN 10216-5 with min 45% can be fulfilled.
Impact strength
Due to its austenitic microstructure, Sandvik 2RE10 has very good impact strength both at room temperature and at cryogenic temperatures.
Tests have demonstrated that the steel fulfils requirements according to the European standards prEN 13445-2 (UFPV-2) ( (min. 60 J (44 ft-lb) at -270
o
C (-455
o
F)) and EN 10216-5 (min. 60 J (44 ft-lb) at -196
o
C (-320
o
F).
At high temperatures
Metric units
Temperature, °C
Proof strength
R
p0.2
MPa
min.
R
p1.0
MPa
min.
Tensile strength
R
m
MPa
min.
50
100
150
200
250
300
350
400
195
180
170
160
150
145
140
135
225
210
200
190
180
170
165
160
485
470
455
440
430
420
415
410
Imperial units
Temperature, °F
Proof strength
R
p0.2
ksi
min.
R
p1.0
ksi
min.
Tensile strength
R
m
ksi
min.
200
400
600
700
26.4
23.1
20.8
20.0
30.8
27.4
24.4
23.6
68.5
63.7
60.7
59.9
.